Arkema Group Oroglas® V 045 I Acrylic, Extrusion Grade (discontinued **)
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
OROGLAS V 045 I is an extrusion that exhibits the following properties : 50% tougher than standard acrylics excellent optical properties ( comparable to that of standard acrylics) superior surface quality The properties enhancement translates into the following benefits : improved handling durability ( in plant, in transit and in service ) improved yields and reduced reject rates. OROGLAS V 045 I is recommended for extrusion applications in replacement of dry blend approach ( impact acrylics + standard acrylics )OROGLAS V 045 I is suitable for most of the extrusion applications: profiles, tubes and sheets.ISO data provided by the manufacturer, Arkema.Arkema, formed in 2004, was formerly Atofina Chemicals and before that Elf Atochem.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | |
| Water Absorption | 2.0 % | 2.0 % | |
| Moisture Absorption at Equilibrium | 0.30 % | 0.30 % | Humidity Absorption |
| Melt Flow | 1.8 g/10 min
@Load 3.80 kg,
Temperature 230 °C |
1.8 g/10 min
@Load 8.38 lb,
Temperature 446 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 78.0 MPa | 11300 psi | 50 mm/min |
| Elongation at Break | 10 % | 10 % | Nominal Strain; 50 mm/min |
| Tensile Modulus | 3.00 GPa | 435 ksi | 1 mm/min |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | |
| Charpy Impact, Notched | 0.250 J/cm² | 1.19 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 2600 MPa | 377000 psi | |
| Tensile Creep Modulus, 1000 hours | 1700 MPa | 247000 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C
@Temperature 20.0 °C
|
38.9 µin/in-°F
@Temperature 68.0 °F
|
|
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C | 201 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 91.0 °C | 196 °F | |
| Vicat Softening Point | 92.0 °C | 198 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB
@Thickness 1.60 mm
|
HB
@Thickness 0.0630 in
|
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 80 % | 80 % | Mfr. reports ‘Transparent’ but doesn’t quantify. |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 3.2
@Frequency 1e+6 Hz
|
3.2
@Frequency 1e+6 Hz
|
|
| 3.7
@Frequency 100 Hz
|
3.7
@Frequency 100 Hz
|
||
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | |
| Dissipation Factor | 0.040
@Frequency 1e+6 Hz
|
0.040
@Frequency 1e+6 Hz
|
|
| 0.050
@Frequency 100 Hz
|
0.050
@Frequency 100 Hz
|
||
| Comparative Tracking Index | 600 V | 600 V |