BASF Ultrason® E 2010 G4 MR SW 15102 20% Glass Filled PESU
| Manufacturer | BASF |
| Trade Name | Ultrason® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.700 – 0.800 g/cc | 0.0253 – 0.0289 lb/in³ | |
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| Water Absorption | 1.6 % | 1.6 % | ISO 62 |
| Moisture Absorption at Equilibrium | 0.60 % | 0.60 % | 23°C; 50% RH; ISO 62 |
| Viscosity Measurement | 56 | 56 | [cm<sup>3</sup>/g]; ISO 307 |
| Linear Mold Shrinkage, Flow | 0.0036 cm/cm | 0.0036 in/in | ISO 2577, 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0061 cm/cm | 0.0061 in/in | ISO 2577, 294-4 |
| Melt Flow | 43.5 g/10 min
@Load 10.0 kg,
Temperature 360 °C |
43.5 g/10 min
@Load 22.0 lb,
Temperature 680 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 205 MPa
@Load 98.0 kg,
Time 30.0 sec |
29700 psi
@Load 216 lb,
Time 0.00833 hour |
ISO 2039-1 |
| Tensile Strength at Break | 125 MPa | 18100 psi | ISO 527-1/-2 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527-1/-2 |
| Tensile Modulus | 7.30 GPa | 1060 ksi | ISO 527-1/-2 |
| Izod Impact, Notched (ISO) | 6.50 kJ/m² | 3.09 ft-lb/in² | ISO 180/A |
| Charpy Impact Unnotched | 4.70 J/cm² | 22.4 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.650 J/cm² | 3.09 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C
@Temperature 23.0 – 80.0 °C
|
11.1 µin/in-°F
@Temperature 73.4 – 176 °F
|
ISO 75-1/-2 |
| 23.0 µm/m-°C
@Temperature 180 °C
|
12.8 µin/in-°F
@Temperature 356 °F
|
DIN 53752 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75-1/-2 |
| Glass Transition Temp, Tg | 225 °C | 437 °F | ISO 11357-1/-2 |
| Decomposition Temperature | >= 400 °C | >= 752 °F | |
| Flammability, UL94 | V-0
@Thickness 1.60 mm
|
V-0
@Thickness 0.0630 in
|
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 80.0 °C | 176 °F | Hopper throat |
| Zone 1 | 350 °C | 662 °F | Feed zone |
| Zone 2 | 360 °C | 680 °F | Compression |
| Zone 3 | 370 °C | 698 °F | Metering-zone |
| Zone 4 | 370 °C | 698 °F | Nozzle |
| Melt Temperature | 350 – 390 °C | 662 – 734 °F | Injection molding/extrusion |
| 370 °C | 698 °F | Optimal | |
| Mold Temperature | 150 – 190 °C | 302 – 374 °F | Injection molding |
| 170 °C | 338 °F | Optimal | |
| Drying Temperature | 140 °C | 284 °F | |
| Dry Time | 4 hour | 4 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Commercial Status | Europe | |
| Ignition Temperature | 580-600°C | DIN 54836 |
| Primary Processing Technique | Injection molding |