LATI Lapex A G/20 PES, 20% Glass Fiber Reinforced
| Manufacturer | LATI |
| Trade Name | Lapex |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Polyether Sulfone (PES) based compound. Glass fibers. Low smoke density and low toxicity index. Very high dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0035 – 0.0050 cm/cm | 0.0035 – 0.0050 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0075 – 0.0090 cm/cm | 0.0075 – 0.0090 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa
@Temperature 150 °C
|
11600 psi
@Temperature 302 °F
|
|
| 90.0 MPa
@Temperature 120 °C
|
13100 psi
@Temperature 248 °F
|
||
| 100 MPa
@Temperature 90.0 °C
|
14500 psi
@Temperature 194 °F
|
||
| 110 MPa
@Temperature 60.0 °C
|
16000 psi
@Temperature 140 °F
|
||
| 115 MPa
@Temperature 23.0 °C
|
16700 psi
@Temperature 73.4 °F
|
||
| Elongation at Break | 2.5 %
@Temperature 23.0 °C
|
2.5 %
@Temperature 73.4 °F
|
|
| 2.6 %
@Temperature 60.0 °C
|
2.6 %
@Temperature 140 °F
|
||
| 2.7 %
@Temperature 90.0 °C
|
2.7 %
@Temperature 194 °F
|
||
| 2.8 %
@Temperature 120 °C
|
2.8 %
@Temperature 248 °F
|
||
| 3.0 %
@Temperature 150 °C
|
3.0 %
@Temperature 302 °F
|
||
| Elongation at Yield | 2.5 %
@Temperature 150 °C
|
2.5 %
@Temperature 302 °F
|
|
| Tensile Modulus | 5.90 GPa
@Temperature 150 °C
|
856 ksi
@Temperature 302 °F
|
|
| 6.15 GPa
@Temperature 120 °C
|
892 ksi
@Temperature 248 °F
|
||
| 6.30 GPa
@Temperature 90.0 °C
|
914 ksi
@Temperature 194 °F
|
||
| 6.50 GPa
@Temperature 60.0 °C
|
943 ksi
@Temperature 140 °F
|
||
| 6.70 GPa
@Temperature 23.0 °C
|
972 ksi
@Temperature 73.4 °F
|
||
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 180 °C | 356 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | |
| Vicat Softening Point | 220 °C
@Load 5.00 kg
|
428 °F
@Load 11.0 lb
|
|
| Flammability, UL94 | V-0
@Thickness 3.00 mm
|
V-0
@Thickness 0.118 in
|
|
| V-0
@Thickness 1.50 mm
|
V-0
@Thickness 0.0591 in
|
||
| Oxygen Index | 39 % | 39 % |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 350 – 370 °C | 662 – 698 °F | |
| Mold Temperature | 140 – 165 °C | 284 – 329 °F | |
| Drying Temperature | 150 – 180 °C
@Time 10800 sec
|
302 – 356 °F
@Time 3.00 hour
|
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage – Pressure | 60 MPa |