Braskem LBH0120PBS LLDPE Blown Film Extrusion Polyethylene Copolymer
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
LBH0120BPS is a LLDPE Hexene copolymer produced by Braskem. It is a general purpose product that shows a good processing performance balanced with good optical and mechanical properties as well as sealability. It has a very low gel amount. It contains anitblocking, slip, and processing aid additives. Its applications include automatic packaging (FFS), liners, general purpose, and HDPE and LDPE blends.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM-D792 |
| Melt Flow | 0.75 g/10 min
@Load 2.16 kg,
Temperature 190 °C |
0.75 g/10 min
@Load 4.76 lb,
Temperature 374 °F |
ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 880 % | 880 % | ASTM-D882 |
| Film Elongation at Break, TD | 1140 % | 1140 % | ASTM-D882 |
| Elmendorf Tear Strength MD | 310 g | 310 g | ASTM-D1922 |
| Elmendorf Tear Strength TD | 500 g | 500 g | ASTM-D1922 |
| Elmendorf Tear Strength, MD | 12.4 g/micron | 315 g/mil | ASTM-D1922 |
| Elmendorf Tear Strength, TD | 20.0 g/micron | 508 g/mil | ASTM-D1922 |
| Dart Drop | 7.20 g/micron | 183 g/mil | ASTM-D1709 |
| Dart Drop Test | 180 g | 0.397 lb | ASTM-D1709 |
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM-D882 |
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM-D882 |
| 1% Secant Modulus, MD | 170 MPa | 24700 psi | ASTM-D882 |
| 1% Secant Modulus, TD | 190 MPa | 27600 psi | ASTM-D882 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 23 % | 23 % | ASTM-D1003 |
| Gloss | 76 % | 76 % | Angle 60°; ASTM-D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Die Opening | 0.180 – 0.250 cm | 0.0709 – 0.0984 in | Blown Film Extrusion |
| Blow-up Ratio (BUR) | 2.0 – 3.0 | 2.0 – 3.0 | Blown Film Extrusion |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Mass Temperature (°C) | 190-210 | Blown Film Extrusion |
| Screen Package | 40/40 | 100% pure |
| 40/60/40 | Blend | |
| Temperature Profile (°C) | 180-210 | Blown Film Extrusion |