Diamond Polymers DIAMALOY GLY 7510 High Heat ASA Weatherable Polymer
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Diamaloy GLY 7510 resin is a high gloss, high heat and high impact grade of ASA (acrylonitrile-styrene-acrylate) with good resistance to weather aging. This product is rated f1 by UL and be customed colored.Applications:Typical applications include those requiring weatherability and toughness for automotive exterior applications and lawn and garden applications. As with any product, use of Diamaloy GLY 7510 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 – 0.0070 cm/cm | 0.0040 – 0.0070 in/in | ASTM D955 |
| Melt Flow | 4.0 g/10 min
@Load 10.0 kg,
Temperature 220 °C |
4.0 g/10 min
@Load 22.0 lb,
Temperature 428 °F |
ASTM D1238 |
| 8.3 g/10 min
@Load 5.00 kg,
Temperature 260 °C |
8.3 g/10 min
@Load 11.0 lb,
Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 101 | 101 | ASTM D785 |
| Tensile Strength at Break | 38.0 MPa | 5510 psi | chs 2.0 in/min; ASTM D638 |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | chs 2.0 in/min; ASTM D638 |
| Elongation at Break | 22 % | 22 % | chs 2.0 in/min; ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | chs 2.0 in/min; ASTM D638 |
| Tensile Modulus | 2.784 GPa | 403.8 ksi | chs 2.0 in/min; ASTM D638 |
| Flexural Strength | 79.0 MPa
@Thickness 3.17 mm
|
11500 psi
@Thickness 0.125 in
|
chs 0.05 in/min; 2 in span; ASTM D790 |
| Flexural Modulus | 2.432 GPa
@Thickness 3.17 mm
|
352.7 ksi
@Thickness 0.125 in
|
chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm
@Thickness 3.17 mm,
Temperature -30.0 °C |
0.800 ft-lb/in
@Thickness 0.125 in,
Temperature -22.0 °F |
ASTM D256 |
| 2.46 J/cm
@Thickness 3.17 mm,
Temperature 23.0 °C |
4.61 ft-lb/in
@Thickness 0.125 in,
Temperature 73.4 °F |
ASTM D256 | |
| Impact Test | 20.8 J
@Temperature -30.0 °C
|
15.3 ft-lb
@Temperature -22.0 °F
|
Total Energy; ASTM D3763 |
| 27.0 J
@Temperature 23.0 °C
|
19.9 ft-lb
@Temperature 73.4 °F
|
Total Energy; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 75.6 µm/m-°C
@Temperature -40.0 – 37.8 °C
|
42.0 µin/in-°F
@Temperature -40.0 – 100 °F
|
ASTM E831 |
| CTE, linear, Transverse to Flow | 86.4 µm/m-°C
@Temperature -40.0 – 37.8 °C
|
48.0 µin/in-°F
@Temperature -40.0 – 100 °F
|
ASTM E831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 102 °C | 216 °F | 0.125″;; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | 0.125″;; ASTM D648 |
| Vicat Softening Point | 104 °C | 219 °F | ASTM D1525 |
| Flammability, UL94 | HB
@Thickness 1.52 mm
|
HB
@Thickness 0.0600 in
|
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 94 % | 94 % | Untextured; 60°; ASTM D523 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Wire Ignition, HWI | 3.0 sec | 3.0 sec | PLC Code; ASTM 746A |
| High Amp Arc Ignition, HAI | 0.00 arcs | 0.00 arcs | PLC Code; ASTM 746A |