Lanxess Durethan® B 35 FKA 000000 Nylon 6, Film Grade
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
PA 6 Film grade, medium viscosity, nucleated, with processing and slip additives, in compliance with FDA for food contactApplication Examples: flat and blown film, flat film coextrusion for PA/PE composite films
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ISO 1183 |
| Water Absorption | 10 % | 10 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 3.0 % | 3.0 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Melt Flow | 8 g/10 min
@Load 2.16 kg,
Temperature 235 °C |
8 g/10 min
@Load 4.76 lb,
Temperature 455 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | Conditioned; ISO 527-1/-2 |
| 75.0 MPa | 10900 psi | ISO 527-1/-2 | |
| Elongation at Break | 20 % | 20 % | Nominal; ISO 527-1/-2 |
| >= 50 % | >= 50 % | Nominal, Conditioned; ISO 527-1/-2 | |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527-1/-2 |
| 25 % | 25 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 0.800 GPa | 116 ksi | Conditioned; ISO 527-1/-2 |
| 2.80 GPa | 406 ksi | ISO 527-1/-2 | |
| Charpy Impact Unnotched | NB
@Temperature -30.0 °C
|
NB
@Temperature -22.0 °F
|
ISO 179/1eU |
| NB
@Temperature -30.0 °C
|
NB
@Temperature -22.0 °F
|
Conditioned; ISO 179/1eU | |
| NB
@Temperature 23.0 °C
|
NB
@Temperature 73.4 °F
|
ISO 179/1eU | |
| NB
@Temperature 23.0 °C
|
NB
@Temperature 73.4 °F
|
Conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 0.500 J/cm²
@Temperature -30.0 °C
|
2.38 ft-lb/in²
@Temperature -22.0 °F
|
ISO 179/1eA |
| <= 0.500 J/cm²
@Temperature -30.0 °C
|
<= 2.38 ft-lb/in²
@Temperature -22.0 °F
|
Conditioned; ISO 179/1eA | |
| 0.500 J/cm²
@Temperature 23.0 °C
|
2.38 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/1eA | |
| 5.00 J/cm²
@Temperature 23.0 °C
|
23.8 ft-lb/in²
@Temperature 73.4 °F
|
Conditioned; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 222 °C | 432 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 40.0 °C | 104 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB
@Thickness 1.60 mm
|
HB
@Thickness 0.0630 in
|
IEC 60695-11-10 |
| HB
@Thickness 3.20 mm
|
HB
@Thickness 0.126 in
|
IEC 60695-11-10 | |
| Oxygen Index | 24 % | 24 % | ISO 4589-1/-2 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Conditioned; IEC 60093 |
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 3.5
@Frequency 1.00e+6 Hz
|
3.5
@Frequency 1.00e+6 Hz
|
IEC 60250 |
| 3.9
@Frequency 100 Hz
|
3.9
@Frequency 100 Hz
|
IEC 60250 | |
| 4.0
@Frequency 1.00e+6 Hz
|
4.0
@Frequency 1.00e+6 Hz
|
Conditioned; IEC 60250 | |
| 18
@Frequency 100 Hz
|
18
@Frequency 100 Hz
|
Conditioned; IEC 60250 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 |
| 35.0 kV/mm | 889 kV/in | Conditioned; IEC 60243-1 | |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Pellets | |
| ISO Shortname | ISO 1874: PA 6, FS,18,-030N | |
| Processing | Film extrusion | |