LATI Lapex A G/10 PES, 10% Glass Fiber Reinforced
| Manufacturer | LATI |
| Trade Name | Lapex |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Polyether Sulfone (PES) based compound. Glass fibers. Low smoke density and low toxicity index. Very high dimensional stability.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0040 – 0.0055 cm/cm | 0.0040 – 0.0055 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0080 – 0.0095 cm/cm | 0.0080 – 0.0095 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa
@Temperature 150 °C
|
10200 psi
@Temperature 302 °F
|
|
| 75.0 MPa
@Temperature 120 °C
|
10900 psi
@Temperature 248 °F
|
||
| 90.0 MPa
@Temperature 90.0 °C
|
13100 psi
@Temperature 194 °F
|
||
| 95.0 MPa
@Temperature 60.0 °C
|
13800 psi
@Temperature 140 °F
|
||
| 100 MPa
@Temperature 23.0 °C
|
14500 psi
@Temperature 73.4 °F
|
||
| Elongation at Break | 3.5 %
@Temperature 23.0 °C
|
3.5 %
@Temperature 73.4 °F
|
|
| 3.7 %
@Temperature 60.0 °C
|
3.7 %
@Temperature 140 °F
|
||
| 4.1 %
@Temperature 90.0 °C
|
4.1 %
@Temperature 194 °F
|
||
| 4.4 %
@Temperature 120 °C
|
4.4 %
@Temperature 248 °F
|
||
| 20 %
@Temperature 150 °C
|
20 %
@Temperature 302 °F
|
||
| Elongation at Yield | 3.2 %
@Temperature 150 °C
|
3.2 %
@Temperature 302 °F
|
|
| Tensile Modulus | 4.10 GPa
@Temperature 150 °C
|
595 ksi
@Temperature 302 °F
|
|
| 4.30 GPa
@Temperature 120 °C
|
624 ksi
@Temperature 248 °F
|
||
| 4.40 GPa
@Temperature 90.0 °C
|
638 ksi
@Temperature 194 °F
|
||
| 4.50 GPa
@Temperature 60.0 °C
|
653 ksi
@Temperature 140 °F
|
||
| 4.60 GPa
@Temperature 23.0 °C
|
667 ksi
@Temperature 73.4 °F
|
||
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | |
| Charpy Impact, Notched | 0.350 J/cm² | 1.67 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 180 °C | 356 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | |
| Vicat Softening Point | 220 °C
@Load 5.00 kg
|
428 °F
@Load 11.0 lb
|
|
| Flammability, UL94 | V-0
@Thickness 3.00 mm
|
V-0
@Thickness 0.118 in
|
|
| V-0
@Thickness 1.50 mm
|
V-0
@Thickness 0.0591 in
|
||
| Oxygen Index | 39 % | 39 % |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 350 – 370 °C | 662 – 698 °F | |
| Mold Temperature | 140 – 165 °C | 284 – 329 °F | |
| Drying Temperature | 150 – 180 °C
@Time 10800 sec
|
302 – 356 °F
@Time 3.00 hour
|
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage – Pressure | 60 MPa |