LNP Thermocomp® LF-1006 MG Polyetheretherketone, Glass milled Glass Fiber (discontinued **)
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Features: Low WarpageForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names instituted after the SABIC purchase.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.53 g/cc | 1.53 g/cc | Method A; ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 139 MPa | 20200 psi | ASTM D638 |
| Elongation at Break | 2.2 % | 2.2 % | ASTM D638 |
| Tensile Modulus | 9.72 GPa | 1410 ksi | ASTM D638 |
| Flexural Strength | 207 MPa | 30000 psi | ASTM D790 |
| Flexural Modulus | 9.38 GPa | 1360 ksi | ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm
@Thickness 3.18 mm
|
0.500 ft-lb/in
@Thickness 0.125 in
|
ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 379 – 388 °C | 714 – 730 °F | |
| Mold Temperature | 135 – 163 °C | 275 – 325 °F | |
| Drying Temperature | 121 – 149 °C | 250 – 300 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.10 % | 0.10 % | Suggested |
| Back Pressure | 0.345 – 0.689 MPa | 50.0 – 99.9 psi |