Overview of materials for Thermoplastic Polyimide, Carbon Fiber
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Thermoplastic Polyimide, Carbon Fiber”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 – 1.51 g/cc | 0.0499 – 0.0546 lb/in³ | Average value: 1.44 g/cc Grade Count:10 |
| Filler Content | 20.0 – 30.0 % | 20.0 – 30.0 % | Average value: 26.7 % Grade Count:3 |
| Water Absorption | 0.100 – 0.690 % | 0.100 – 0.690 % | Average value: 0.257 % Grade Count:4 |
| 0.660 – 4.17 %
@Temperature 80.0 – 80.0 °C
|
0.660 – 4.17 %
@Temperature 176 – 176 °F
|
Average value: 2.33 % Grade Count:2 | |
| 2.24 – 2.24 %
@Temperature 80.0 – 80.0 °C
|
2.24 – 2.24 %
@Temperature 176 – 176 °F
|
Average value: 2.33 % Grade Count:1 | |
| 2.24 – 2.24 %
@Time 86400 – 86400 sec
|
2.24 – 2.24 %
@Time 24.0 – 24.0 hour
|
Average value: 2.33 % Grade Count:1 | |
| Linear Mold Shrinkage | 0.000100 – 0.00400 cm/cm | 0.000100 – 0.00400 in/in | Average value: 0.00183 cm/cm Grade Count:6 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 89.0 – 91.0 | 89.0 – 91.0 | Average value: 90.0 Grade Count:3 |
| Tensile Strength, Ultimate | 36.5 – 241 MPa | 5300 – 35000 psi | Average value: 174 MPa Grade Count:7 |
| Elongation at Break | 0.800 – 5.50 % | 0.800 – 5.50 % | Average value: 2.17 % Grade Count:6 |
| Elongation at Yield | 1.80 – 4.30 % | 1.80 – 4.30 % | Average value: 2.67 % Grade Count:5 |
| Modulus of Elasticity | 4.50 – 29.0 GPa | 653 – 4200 ksi | Average value: 16.5 GPa Grade Count:8 |
| Flexural Yield Strength | 97.9 – 345 MPa | 14200 – 50000 psi | Average value: 225 MPa Grade Count:10 |
| Flexural Modulus | 4.24 – 25.5 GPa | 615 – 3700 ksi | Average value: 12.6 GPa Grade Count:10 |
| Compressive Yield Strength | 184 – 474 MPa | 26700 – 68700 psi | Average value: 279 MPa Grade Count:4 |
| Izod Impact, Notched | 0.801 – 1.07 J/cm | 1.50 – 2.00 ft-lb/in | Average value: 0.921 J/cm Grade Count:4 |
| Izod Impact, Unnotched | 4.81 – 6.41 J/cm | 9.00 – 12.0 ft-lb/in | Average value: 5.94 J/cm Grade Count:4 |
| Charpy Impact Unnotched | 1.96 – 3.74 J/cm² | 9.33 – 17.8 ft-lb/in² | Average value: 2.90 J/cm² Grade Count:3 |
| 3.50 – 3.50 J/cm²
@Temperature -30.0 – -30.0 °C
|
16.7 – 16.7 ft-lb/in²
@Temperature -22.0 – -22.0 °F
|
Average value: 3.50 J/cm² Grade Count:1 | |
| Charpy Impact, Notched | 1.00 – 1.00 J/cm²
@Temperature -30.0 – -30.0 °C
|
4.76 – 4.76 ft-lb/in²
@Temperature -22.0 – -22.0 °F
|
Average value: 1.00 J/cm² Grade Count:1 |
| Compression Set | 49.0 – 98.0 % | 49.0 – 98.0 % | Average value: 69.0 % Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 41.0 – 88.0 µm/m-°C
@Temperature 50.0 – 300 °C
|
22.8 – 48.9 µin/in-°F
@Temperature 122 – 572 °F
|
Average value: 61.0 µm/m-°C Grade Count:3 |
| CTE, linear, Transverse to Flow | 43.0 – 67.0 µm/m-°C
@Temperature 50.0 – 300 °C
|
23.9 – 37.2 µin/in-°F
@Temperature 122 – 572 °F
|
Average value: 54.5 µm/m-°C Grade Count:2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 – 340 °C | 464 – 644 °F | Average value: 297 °C Grade Count:5 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:7 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10000 – 1.00e+12 ohm | 10000 – 1.00e+12 ohm | Average value: 1.40e+11 ohm Grade Count:4 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 371 – 410 °C | 700 – 770 °F | Average value: 384 °C Grade Count:3 |
| Melt Temperature | 370 – 416 °C | 698 – 780 °F | Average value: 392 °C Grade Count:5 |
| Mold Temperature | 177 – 232 °C | 350 – 450 °F | Average value: 200 °C Grade Count:6 |
| Drying Temperature | 180 – 204 °C | 356 – 400 °F | Average value: 196 °C Grade Count:5 |
| Moisture Content | 0.0100 % | 0.0100 % | Average value: 0.0100 % Grade Count:3 |
| Dew Point | -40.0 °C | -40.0 °F | Average value: -40.0 °C Grade Count:3 |
| Injection Pressure | 138 – 193 MPa | 20000 – 28000 psi | Average value: 165 MPa Grade Count:4 |