Permabond 2011 Cyanoacrylate, gel
| Manufacturer | Permabond |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
PERMABOND® 2011 is a thixotropic, fast-setting cyanoacrylate particularly suitable for use on vertical and porous substrates. This material can be used on metals, plastics, elastomers, ceramics and wood. Cyanoacrylate adhesives are single component adhesives that polymerize rapidly when pressed into a thin film between parts. The moisture adsorbed on the surface initiates the curing of the adhesive. Strong bonds are developed extremely fast and on a great variety of materials. These properties make PERMABOND cyanoacrylates the ideal adhesives for high speed production lines. Features & Benefits: Thixotropic Surface insensitive Fast cure Easy to apply and dispense High temperature resistance Maximum gap filling capability Information provided by Permabond.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | Uncured |
| 1.10 g/cc | 1.10 g/cc | Uncured | |
| Viscosity | 70 – 90 cP
@Temperature 25.0 °C
|
70 – 90 cP
@Temperature 77.0 °F
|
Uncured |
| Storage Temperature | 2.00 – 7.00 °C | 35.6 – 44.6 °F | |
| 2.00 – 7.00 °C | 35.6 – 44.6 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 85 | 85 | ISO 868 |
| 85 | 85 | ISO 868 | |
| Adhesive Bond Strength | >= 2.00 MPa | >= 290 psi | Butyl Rubber, Substrate Failure, Shear; ISO 4587 |
| >= 4.00 MPa | >= 580 psi | Nitrile Rubber, Substrate Failure, Shear; ISO 4587 | |
| >= 5.00 MPa | >= 725 psi | PC, Substrate Failure, Shear; ISO 4587 | |
| >= 6.00 MPa | >= 870 psi | ABS, Substrate Failure, Shear; ISO 4587 | |
| >= 6.00 MPa | >= 870 psi | PVC, Substrate Failure, Shear; ISO 4587 | |
| 8.00 – 9.00 MPa | 1160 – 1310 psi | Aluminum, Shear; ISO 4587 | |
| >= 9.00 MPa | >= 1310 psi | ABS, Substrate Failure, Shear; ISO 4587 | |
| >= 10.0 MPa | >= 1450 psi | Phenolic, Substrate Failure, Shear; ISO 4587 | |
| 10.0 MPa | 1450 psi | Zinc, Shear; ISO 4587 | |
| >= 14.0 MPa | >= 2030 psi | Acrylic, Shear; ISO 4587 | |
| 14.0 MPa | 2030 psi | Phenolic, Shear; ISO 4587 | |
| 13.0 – 15.0 MPa | 1890 – 2180 psi | Aluminum, Shear; ISO 4587 | |
| 21.0 MPa | 3050 psi | Brass, Shear; ISO 4587 | |
| 21.0 MPa | 3050 psi | Stainless Steel, Shear; ISO 4587 | |
| 20.0 – 24.0 MPa | 2900 – 3480 psi | Steel, Shear; ISO 4587 | |
| 23.0 – 29.0 MPa | 3340 – 4210 psi | Steel, Shear; ISO 4587 | |
| Impact | 3.0 – 5.0 | 3.0 – 5.0 | kJ/m<sup>2</sup> Adhesive Impact Strength; ASTM D950 |
| 3.0 – 5.0 | 3.0 – 5.0 | kJ/m<sup>2</sup> Adhesive Impact Strength; ASTM D950 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | |
| 90.0 µm/m-°C | 50.0 µin/in-°F | ||
| Thermal Conductivity | 0.100 W/m-K | 0.694 BTU-in/hr-ft²-°F | |
| 0.100 W/m-K | 0.694 BTU-in/hr-ft²-°F | ||
| Maximum Service Temperature, Air | 82.2 °C | 180 °F | |
| Minimum Service Temperature, Air | -62.2 °C | -80.0 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 2.5
@Frequency 10000 Hz
|
2.5
@Frequency 10000 Hz
|
|
| 2.5
@Frequency 10000 Hz
|
2.5
@Frequency 10000 Hz
|
||
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | |
| 25.0 kV/mm | 635 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 0.0833 – 0.167 min | 0.00139 – 0.00278 hour | Steel, handling time |
| 0.0833 – 0.167 min | 0.00139 – 0.00278 hour | Buna N Rubber, handling time | |
| 0.0833 – 0.167 min | 0.00139 – 0.00278 hour | Phenolic, handling time | |
| 0.167 – 0.250 min | 0.00278 – 0.00417 hour | Steel, handling time | |
| 0.167 – 0.250 min | 0.00278 – 0.00417 hour | Buna N Rubber, handling time | |
| 0.167 – 0.250 min | 0.00278 – 0.00417 hour | Phenolic, handling time | |
| 1440 min | 24.0 hour | full strength | |
| 1440 min | 24.0 hour | full strength |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Colorless | Uncured |
| Colorless Gel | Uncured | |
| Maximum Gap Fill (mm) | 0.15 | |
| 0.5 | ||
| Strength Retention | 100% at 0°C | Relative to 0°C |
| 100% at 0°C | Relative to 0°C | |
| 15% at 150°C | Relative to 0°C | |
| 15% at 150°C | Relative to 0°C | |
| 30% at 100°C | Relative to 0°C | |
| 50% at 100°C | Relative to 0°C | |
| 55% at -50°C | Relative to 0°C | |
| 75% at -50°C | Relative to 0°C | |
| 90% at 50°C | Relative to 0°C | |
| 90% at 50°C | Relative to 0°C |