Permabond HH190 Anaerobic Gasketmaker
| Manufacturer | Permabond |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Permabond® HH190 Gasketmaker is an anaerobic curing flange sealant that can replace, or be used as a dressing for, conventional pre-cut gaskets. Since HH190 is a flowable paste, it conforms to the shape of the flange. The consistency allows metal to metal contact of the flanges while filling the areas where no contact exists because of irregularities. HH190 results in uniform stress distribution and eliminates the need for re-torquing because of stress relaxation of the flange bolts. It provides instant seal depending on the gap and flange width and ultimately seals up to 5000 psi Features & Benefits: Eliminates pre-cut gaskets from flange assemblies Instant pressure seal Forms a tough, durable seal able to withstand high pressure No need to re-tighten flange bolts Non-flammable No shimming effects – better load transmission Information provided by Permabond.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | Uncured |
| Viscosity | 300000 cP
@Temperature 25.0 °C
|
300000 cP
@Temperature 77.0 °F
|
Uncured |
| Storage Temperature | 5.00 – 25.0 °C | 41.0 – 77.0 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Adhesive Bond Strength | 6.00 MPa | 870 psi | steel collar and pin shear; ISO 10123 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 121 °C | 250 °F | |
| Minimum Service Temperature, Air | -53.9 °C | -65.0 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 11.0 kV/mm | 279 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 15.0 min
@Temperature 23.0 °C
|
0.250 hour
@Temperature 73.4 °F
|
M10 steel, handling strength |
| 30.0 min
@Temperature 23.0 °C
|
0.500 hour
@Temperature 73.4 °F
|
Zinc, handling strength | |
| 60.0 min
@Temperature 23.0 °C
|
1.00 hour
@Temperature 73.4 °F
|
Aluminum, handling strength | |
| 60.0 – 180 min
@Temperature 23.0 °C
|
1.00 – 3.00 hour
@Temperature 73.4 °F
|
M10 steel, working strength | |
| 180 – 360 min
@Temperature 23.0 °C
|
3.00 – 6.00 hour
@Temperature 73.4 °F
|
Zinc, working strength | |
| 1440 min
@Temperature 23.0 °C
|
24.0 hour
@Temperature 73.4 °F
|
M10 steel, full strength | |
| 4320 min
@Temperature 23.0 °C
|
72.0 hour
@Temperature 73.4 °F
|
Aluminum, working strength |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Purple | Uncured |
| Maximum Gap Fill (mm) | 0.3 | |
| Strength Retention | 50% at 150°C | Relative to 0°C |
| 80% at 100°C | Relative to 0°C | |
| 93% at 50°C | Relative to 0°C | |
| Torque Strength (N m) | 10 | M10 steel, break |
| 6 | M10 steel, prevail | |
| UV Fluorescence | No | Uncured |