SABIC Innovative Plastics Geloy EXGY30CP ASA
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | GELOY |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Pearlescent GELOY ASA resin with copper-look for capstock extrusion. Outstanding weatherability.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D 792 |
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00 – 0.0010 cm/cm
@Thickness 3.20 mm
|
0.00 – 0.0010 in/in
@Thickness 0.126 in
|
SABIC Method |
| Melt Flow | 0.60 g/10 min
@Load 3.80 kg,
Temperature 200 °C |
0.60 g/10 min
@Load 8.38 lb,
Temperature 392 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 39.0 MPa | 5660 psi | Type I, 5 mm/min; ASTM D 638 |
| 48.0 MPa | 6960 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | Type I, 5 mm/min; ASTM D 638 |
| 50.0 MPa | 7250 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 14 % | 14 % | Type I, 5 mm/min; ASTM D 638 |
| 29 % | 29 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 3.3 % | 3.3 % | Type I, 5 mm/min; ASTM D 638 |
| 3.6 % | 3.6 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.67 GPa | 387 ksi | 5 mm/min; ASTM D 638 |
| 2.75 GPa | 399 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 76.0 MPa | 11000 psi | 2 mm/min; ISO 178 |
| 77.0 MPa | 11200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Modulus | 2.75 GPa | 399 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 2.78 GPa | 403 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.340 J/cm
@Temperature -30.0 °C
|
0.637 ft-lb/in
@Temperature -22.0 °F
|
ASTM D 256 |
| 0.670 J/cm
@Temperature 23.0 °C
|
1.26 ft-lb/in
@Temperature 73.4 °F
|
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 3.00 kJ/m²
@Temperature -30.0 °C
|
1.43 ft-lb/in²
@Temperature -22.0 °F
|
80*10*4; ISO 180/1A |
| 6.00 kJ/m²
@Temperature 23.0 °C
|
2.86 ft-lb/in²
@Temperature 73.4 °F
|
80*10*4; ISO 180/1A | |
| Impact Test | 4.00 J
@Temperature 23.0 °C
|
2.95 ft-lb
@Temperature 73.4 °F
|
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 95.4 µm/m-°C
@Temperature -40.0 – 40.0 °C
|
53.0 µin/in-°F
@Temperature -40.0 – 104 °F
|
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 108 µm/m-°C
@Temperature -40.0 – 40.0 °C
|
60.0 µin/in-°F
@Temperature -40.0 – 104 °F
|
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 76.0 °C
@Thickness 3.20 mm
|
169 °F
@Thickness 0.126 in
|
unannealed; ASTM D 648 | |
| Vicat Softening Point | 86.0 °C | 187 °F | Rate B/50; ISO 306 |
| 89.0 °C | 192 °F | Rate B/50; ASTM D 1525 |