Sax Polymers SAXATEC 4120 Acrylonitrile Styrene Acrylate
| Manufacturer | Sax Polymers |
| Trade Name | SAXATEC |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
SAXATEC 4120 is a easy lowing, weatherable ASA injection molding grade, characterized by high impact strength, high stiffness and good resistance to heat distortion.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | |
| Linear Mold Shrinkage | 0.0040 – 0.0070 cm/cm | 0.0040 – 0.0070 in/in | |
| Melt Flow | 21 g/10 min
@Load 10.0 kg,
Temperature 220 °C |
21 g/10 min
@Load 22.0 lb,
Temperature 428 °F |
from MVR; ISO 1033 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 62.0 MPa | 8990 psi | ISO 527-1 |
| Elongation at Break | 10 % | 10 % | ISO 527-1 |
| Tensile Modulus | 2.70 GPa | 392 ksi | ISO 527-1 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m²
@Temperature -30.0 °C
|
2.38 ft-lb/in²
@Temperature -22.0 °F
|
ISO 180/1A |
| 7.00 kJ/m²
@Temperature 23.0 °C
|
3.33 ft-lb/in²
@Temperature 73.4 °F
|
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m²
@Temperature -30.0 °C
|
19.0 ft-lb/in²
@Temperature -22.0 °F
|
ISO 180 |
| 80.0 kJ/m²
@Temperature 23.0 °C
|
38.1 ft-lb/in²
@Temperature 73.4 °F
|
ISO 180 | |
| Charpy Impact Unnotched | 6.00 J/cm²
@Temperature -30.0 °C
|
28.6 ft-lb/in²
@Temperature -22.0 °F
|
ISO 179/1eU |
| 10.0 J/cm²
@Temperature 23.0 °C
|
47.6 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/1eU | |
| Charpy Impact, Notched | 0.500 J/cm²
@Temperature -30.0 °C
|
2.38 ft-lb/in²
@Temperature -22.0 °F
|
ISO 179/1eA |
| 0.700 J/cm²
@Temperature 23.0 °C
|
3.33 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Hot Ball Pressure Test | 95.0 °C
@Thickness 2.00 mm
|
203 °F
@Thickness 0.0787 in
|
IE/CEN 60335-1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 89.0 °C | 192 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 104 °C | 219 °F | 50B; ISO 306 |
| Glow Wire Test | 750 °C | 1380 °F | IEC 60695-2-12 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 – 260 °C | 428 – 500 °F | |
| Mold Temperature | 60.0 – 90.0 °C | 140 – 194 °F | |
| Drying Temperature | 80.0 °C
@Time 7200 – 21600 sec
|
176 °F
@Time 2.00 – 6.00 hour
|
|
| Moisture Content | <= 0.20 % | <= 0.20 % |