Solvay Specialty Polymers AvaSpire® AV-750 GF40 Polyaryletherketone (PAEK) (Unverified Data**)
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
AvaSpire AV-750 GF40 is a 40% glass reinforced polyaryletherketone (PAEK) designed to fill the marketplace need for a lower-priced PEEK (polyetheretherketone). This resin provides the typical chemical resistance expected of PEEK while maintaining excellent elevated temperature properties. The price and performance of this resin will expand the opportunities for PEEK resins especially in the area of metal replacement for corrosion control. – Natural: AvaSpire AV-750 GF40 NTInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.65 g/cc | 1.65 g/cc | ASTM D792 |
| Filler Content | 40 % | 40 % | Glass Fiber Reinforcement |
| Water Absorption | 0.10 %
@Time 86400 sec
|
0.10 %
@Time 24.0 hour
|
ASTM D570 |
| Viscosity | 450000 cP
@Shear Rate 1000 1/s,
Temperature 400 °C |
450000 cP
@Shear Rate 1000 1/s,
Temperature 752 °F |
Melt; ASTM D3835 |
| Linear Mold Shrinkage, Flow | 0.0010 – 0.0030 cm/cm
@Thickness 3.18 mm
|
0.0010 – 0.0030 in/in
@Thickness 0.125 in
|
5″ x 0.5″ x 0.125″ bars; ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.012 – 0.014 cm/cm
@Thickness 3.18 mm
|
0.012 – 0.014 in/in
@Thickness 0.125 in
|
5″ x 0.5″ x 0.125″ bars; ASTM D955 |
| Melt Flow | 7.0 g/10 min
@Load 2.16 kg,
Temperature 380 °C |
7.0 g/10 min
@Load 4.76 lb,
Temperature 716 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 105 | 105 | M-Scale; ASTM D785 |
| Tensile Strength | 191 MPa | 27700 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 188 MPa | 27300 psi | 5 nm; ISO 527-2/1A/5 |
| Elongation at Break | 1.8 % | 1.8 % | 5.0 mm/min; ASTM D638 |
| 1.8 % | 1.8 % | ISO 527-2/1A/5 | |
| Tensile Modulus | 15.1 GPa | 2190 ksi | 5.0 mm/min; ASTM D638 |
| 16.7 GPa | 2420 ksi | ISO 527-2/1A/1 | |
| Flexural Strength | 250 MPa | 36300 psi | ISO 178 |
| 54.0 MPa
@Temperature 250 °C
|
7830 psi
@Temperature 482 °F
|
ASTM D790 | |
| 253 MPa
@Temperature 23.0 °C
|
36700 psi
@Temperature 73.4 °F
|
ASTM D790 | |
| Flexural Modulus | 14.8 GPa | 2150 ksi | ASTM D790 |
| 15.4 GPa | 2230 ksi | ISO 178 | |
| Compressive Strength | 182 MPa | 26400 psi | ASTM D695 |
| Shear Strength | 89.0 MPa | 12900 psi | ASTM D732 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| 5.90 J/cm | 11.1 ft-lb/in | ASTM D4812 | |
| Izod Impact, Notched (ISO) | 8.50 kJ/m² | 4.04 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | 41.0 kJ/m² | 19.5 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C
@Temperature -50.0 – 50.0 °C
|
8.33 µin/in-°F
@Temperature -58.0 – 122 °F
|
TMA; ASTM E831 |
| Specific Heat Capacity | 1.26 J/g-°C
@Temperature 50.0 °C
|
0.301 BTU/lb-°F
@Temperature 122 °F
|
DSC |
| 1.62 J/g-°C
@Temperature 200 °C
|
0.387 BTU/lb-°F
@Temperature 392 °F
|
DSC | |
| Thermal Conductivity | 0.310 W/m-K | 2.15 BTU-in/hr-ft²-°F | ASTM E1530 |
| Melting Point | 345 °C | 653 °F | Peak; ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | Annealed; ASTM D648 |
| Glass Transition Temp, Tg | 150 °C | 302 °F | ASTM D3418 |
| Flammability, UL94 | V-1
@Thickness 0.800 mm
|
V-1
@Thickness 0.0315 in
|
UL 94 |
| V-0
@Thickness 1.60 mm
|
V-0
@Thickness 0.0630 in
|
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.80e+17 ohm-cm | 1.80e+17 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.90e+17 ohm | >= 1.90e+17 ohm | ASTM D257 |
| Dielectric Constant | 3.66
@Frequency 1.00e+6 Hz
|
3.66
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| 3.68
@Frequency 60.0 Hz
|
3.68
@Frequency 60.0 Hz
|
ASTM D150 | |
| 3.69
@Frequency 1000 Hz
|
3.69
@Frequency 1000 Hz
|
ASTM D150 | |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | ASTM D149 |
| Dissipation Factor | 0.0010
@Frequency 1000 Hz
|
0.0010
@Frequency 1000 Hz
|
ASTM D150 |
| 0.0020
@Frequency 60.0 Hz
|
0.0020
@Frequency 60.0 Hz
|
ASTM D150 | |
| 0.0030
@Frequency 1.00e+6 Hz
|
0.0030
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 370 – 395 °C | 698 – 743 °F | |
| Mold Temperature | 175 – 210 °C | 347 – 410 °F | |
| Drying Temperature | 150 – 175 °C | 302 – 347 °F | |
| Dry Time | 2.50 – 4.00 hour | 2.50 – 4.00 hour | |
| Back Pressure | 0.138 – 0.345 MPa | 20.0 – 50.0 psi | |
| Screw Speed | 75 rpm | 75 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Natural Color | |
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Features | Flame Retardant | |
| Good Chemical Resistance | ||
| Good Dimensional Stability | ||
| High Heat Resistance | ||
| High Stiffness | ||
| High Strength | ||
| Forms | Pellets | |
| Generic | PAEK | |
| Processing Method | Injection Molding | |
| Machining | ||
| Profile Extrusion | ||
| RoHS Compliance | RoHS Compliant | |
| Screw Compression Ratio | 2.0:1.0 | |
| Uses | Aircraft Applications | |
| Electrical/Electronic Applications | ||
| Metal Replacement | ||
| Seals |