Solvay Specialty Polymers AvaSpire® AV-650 GF30 Polyaryletherketone (PAEK), 30% Glass Fiber
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | AvaSpire® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
AvaSpire® AV-650 GF30 is a 30% glass fiber-reinforced polyaryletherketone (PAEK) that has been specifically formulated to provide a high degree of chemical resistance and higher mechanical strength and stiffness than unfilled AV-650 resin. This material can be repeatedly exposed to harsh chemicals and prolonged steam sterilization cycles without any significant loss of properties. Potential applications for this resin include orthopedic and dental instruments, surgical power tool battery housings and other devices and components requiring a combination of high temperature performance and high environmental resistance. AvaSpire® AV-650 GF30 can be easily processed by typical injection molding and extrusion methods using standard equipment.Features: Fatigue Resistant; Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; High Heat Resistance; High Stiffness; High StrengthUses: Medical/Healthcare Applications; Oil/Gas Applications; Power/Other ToolsAdditional Properties: Water Absorption – ASTM D570 0.40 %Information provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ASTM D792 |
| Filler Content | 30 % | 30 % | Glass Fiber |
| Water Absorption | 0.20 %
@Time 86400 sec
|
0.20 %
@Time 24.0 hour
|
ISO 62 |
| Viscosity | 410000 cP
@Shear Rate 1000 1/s,
Temperature 400 °C |
410000 cP
@Shear Rate 1000 1/s,
Temperature 752 °F |
Melt Viscosity; ASTM D3835 |
| Linear Mold Shrinkage, Flow | 0.0010 – 0.0030 cm/cm
@Thickness 3.18 mm
|
0.0010 – 0.0030 in/in
@Thickness 0.125 in
|
|
| Linear Mold Shrinkage, Transverse | 0.0080 – 0.010 cm/cm
@Thickness 3.18 mm
|
0.0080 – 0.010 in/in
@Thickness 0.125 in
|
ASTM D955 |
| Melt Flow | 15 g/10 min
@Load 2.16 kg,
Temperature 400 °C |
15 g/10 min
@Load 4.76 lb,
Temperature 752 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 100 | 100 | ASTM D785 |
| Tensile Strength | 142 MPa | 20600 psi | ASTM D638 |
| Tensile Strength, Yield | 165 MPa | 23900 psi | 5 mm/min, Type 1A; ISO 527-2 |
| Elongation at Break | 2.6 % | 2.6 % | Type 1A, 5 mm/min; ISO 527-2 |
| 2.6 % | 2.6 % | 5 mm/min; ASTM D638 | |
| Tensile Modulus | 10.1 GPa | 1460 ksi | ASTM D638 |
| 10.5 GPa | 1520 ksi | ISO 527-2 | |
| Flexural Strength | 221 MPa | 32100 psi | ASTM D790 |
| 240 MPa | 34800 psi | ISO 178 | |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ASTM D790 |
| 9.80 GPa | 1420 ksi | ISO 178 | |
| Compressive Strength | 163 MPa | 23600 psi | ASTM D695 |
| Shear Strength | 80.8 MPa | 11700 psi | ASTM D732 |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.60 J/cm | 18.0 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | 69.0 kJ/m² | 32.8 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 19.0 µm/m-°C
@Temperature -50.0 – 50.0 °C
|
10.6 µin/in-°F
@Temperature -58.0 – 122 °F
|
1 |
| Specific Heat Capacity | 1.29 J/g-°C
@Temperature 50.0 °C
|
0.308 BTU/lb-°F
@Temperature 122 °F
|
ASTM C351 |
| 1.67 J/g-°C
@Temperature 200 °C
|
0.399 BTU/lb-°F
@Temperature 392 °F
|
ASTM C351 | |
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 340 °C | 644 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 209 °C
@Thickness 3.20 mm
|
408 °F
@Thickness 0.126 in
|
Annealed; ASTM D648 |
| Glass Transition Temp, Tg | 158 °C | 316 °F | DSC |
| Flammability, UL94 | V-0
@Thickness 0.800 – 1.60 mm
|
V-0
@Thickness 0.0315 – 0.0630 in
|
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.6
@Frequency 1.00e+6 Hz
|
3.6
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| 3.65
@Frequency 60.0 Hz
|
3.65
@Frequency 60.0 Hz
|
ASTM D150 | |
| 3.66
@Frequency 1000 Hz
|
3.66
@Frequency 1000 Hz
|
ASTM D150 | |
| Dielectric Strength | 14.0 kV/mm
@Thickness 3.18 mm
|
356 kV/in
@Thickness 0.125 in
|
ASTM D149 |
| Dissipation Factor | 0.00
@Frequency 1000 Hz
|
0.00
@Frequency 1000 Hz
|
ASTM D150 |
| 0.0020
@Frequency 60.0 Hz
|
0.0020
@Frequency 60.0 Hz
|
ASTM D150 | |
| 0.0050
@Frequency 1.00e+6 Hz
|
0.0050
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 365 °C | 689 °F | |
| Middle Barrel Temperature | 370 °C | 698 °F | |
| Front Barrel Temperature | 375 °C | 707 °F | |
| Nozzle Temperature | 380 °C | 716 °F | |
| Melt Temperature | 365 – 390 °C | 689 – 734 °F | |
| Mold Temperature | 150 – 180 °C | 302 – 356 °F | |
| Drying Temperature | 150 °C
@Time 14400 sec
|
302 °F
@Time 4.00 hour
|
| Descriptive Properties | Value | Comments |
|---|---|---|
| Agency Ratings | FAA FAR 25.853a | |
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Beige | |
| Form | Pellets | |
| Injection Rate | Fast | |
| Processing Technique | Injection Molding; Machining; Profile Extrusion | |
| Screw Compression Ratio | 2.0:1.0 to 3.0:1.0 |