Solvay Specialty Polymers Veradel® 3320GF Polyethersulfone (PESU), 20% Glass Fiber
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Veradel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Veradel® 3320GF is a 20% glass fiber reinforced grade of polyethersulfone (PESU). Adding glass fiber to polyethersulfone substantially increases the rigidity, tensile strength, creep resistance, dimensional stability and chemical resistance of the material, while maintaining most of its other basic characteristics. The combination of structural properties and cost effectiveness make this resin an attractive alternative to metals in many engineering applications. Veradel® 3320GF is an opaque, grayish material in its natural form and can be readily colored.Features: Acid Resistant; Flame Retardant; Good Adhesion; Good Creep Resistance; Good Dimensional Stability; High Rigidity; High Tensile Strength; Hydrolysis Resistant; Medium Flow; Medium Molecular WeightUses: Metal ReplacementInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ASTM D792 |
| Filler Content | 20 % | 20 % | Glass Fiber |
| Water Absorption | 0.50 %
@Time 86400 sec
|
0.50 %
@Time 24.0 hour
|
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 120 MPa | 17400 psi | ASTM D638 |
| Elongation at Break | 2.8 % | 2.8 % | ASTM D638 |
| Tensile Modulus | 7.00 GPa | 1020 ksi | ASTM D638 |
| Flexural Strength | 170 MPa | 24700 psi | ASTM D790 |
| Flexural Modulus | 6.50 GPa | 943 ksi | ASTM D790 |
| Izod Impact, Notched | 0.700 J/cm | 1.31 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C | 13.9 µin/in-°F | |
| Maximum Service Temperature, Air | 190 °C | 374 °F | Continuous Use |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | Annealed; ASTM D648 |
| Flammability, UL94 | V-0
@Thickness 0.800 mm
|
V-0
@Thickness 0.0315 in
|
|
| Oxygen Index | 42 % | 42 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | ASTM D257 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | ASTM D149 |
| Arc Resistance | 110 sec | 110 sec | ASTM D495 |
| Comparative Tracking Index | 150 V | 150 V | UL 746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 340 – 380 °C | 644 – 716 °F | |
| Mold Temperature | 120 – 160 °C | 248 – 320 °F | |
| Die Cooling Temperature | 300 – 320 °C | 572 – 608 °F | |
| Drying Temperature | 150 °C
@Time 10800 sec
|
302 °F
@Time 3.00 hour
|
|
| Screw Speed | 20 – 50 rpm | 20 – 50 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Colors Available; Opaque | |
| Form | Pellets | |
| Processing Technique | Injection Molding | |
| RoHS Compliance | RoHS Compliant |