Solvay Specialty Polymers AvaSpire® AV-750 GF40 Polyaryletherketone (PAEK), 40% Glass Fiber
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | AvaSpire® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
AvaSpire® AV-750 GF40 is a 40% glass reinforced polyaryletherketone (PAEK) designed to fill the marketplace need for a lower-priced PEEK (polyetheretherketone). This resin provides the typical chemical resistance expected of PEEK while maintaining excellent elevated temperature properties.Features: Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; High Heat Resistance; High Stiffness; High StrengthUses: Aircraft Applications; Electrical/Electronic Applications; Metal Replacement; SealsInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in³ | ASTM D792 |
| Filler Content | 40 % | 40 % | Glass Fiber |
| Water Absorption | 0.10 %
@Time 86400 sec
|
0.10 %
@Time 24.0 hour
|
ISO 62 |
| Viscosity | 450000 cP
@Shear Rate 1000 1/s,
Temperature 400 °C |
450000 cP
@Shear Rate 1000 1/s,
Temperature 752 °F |
Melt Viscosity; ASTM D3835 |
| Linear Mold Shrinkage, Flow | 0.0010 – 0.0030 cm/cm
@Thickness 3.18 mm
|
0.0010 – 0.0030 in/in
@Thickness 0.125 in
|
|
| Linear Mold Shrinkage, Transverse | 0.012 – 0.014 cm/cm
@Thickness 3.18 mm
|
0.012 – 0.014 in/in
@Thickness 0.125 in
|
ASTM D955 |
| Melt Flow | 7.0 g/10 min
@Load 2.16 kg,
Temperature 380 °C |
7.0 g/10 min
@Load 4.76 lb,
Temperature 716 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 105 | 105 | ASTM D785 |
| Tensile Strength | 191 MPa | 27700 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 188 MPa
@Thickness 5.00 mm
|
27300 psi
@Thickness 0.197 in
|
5 mm/min, Type 1A; ISO 527-2 |
| Elongation at Break | 1.8 % | 1.8 % | Type 1A, 5 mm/min; ISO 527-2 |
| 1.8 % | 1.8 % | 5 mm/min; ASTM D638 | |
| Tensile Modulus | 15.1 GPa | 2190 ksi | 5 mm/min; ASTM D638 |
| 16.7 GPa | 2420 ksi | 1 mm/min, Type 1A; ISO 527-2 | |
| Flexural Strength | 250 MPa | 36300 psi | ISO 178 |
| 54.0 MPa
@Temperature 250 °C
|
7830 psi
@Temperature 482 °F
|
ASTM D790 | |
| 253 MPa
@Temperature 23.0 °C
|
36700 psi
@Temperature 73.4 °F
|
ASTM D790 | |
| Flexural Modulus | 14.8 GPa | 2150 ksi | ASTM D790 |
| 15.4 GPa | 2230 ksi | ISO 178 | |
| Compressive Strength | 182 MPa | 26400 psi | ASTM D695 |
| Shear Strength | 89.0 MPa | 12900 psi | ASTM D732 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.90 J/cm | 11.1 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 8.50 kJ/m² | 4.04 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | 41.0 kJ/m² | 19.5 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C
@Temperature -50.0 – 50.0 °C
|
8.33 µin/in-°F
@Temperature -58.0 – 122 °F
|
1 |
| Specific Heat Capacity | 1.26 J/g-°C
@Temperature 50.0 °C
|
0.301 BTU/lb-°F
@Temperature 122 °F
|
ASTM C351 |
| 1.62 J/g-°C
@Temperature 200 °C
|
0.387 BTU/lb-°F
@Temperature 392 °F
|
ASTM C351 | |
| Thermal Conductivity | 0.310 W/m-K | 2.15 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 345 °C | 653 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | Annealed; ASTM D648 |
| Glass Transition Temp, Tg | 150 °C | 302 °F | DSC |
| Flammability, UL94 | V-1
@Thickness 0.800 mm
|
V-1
@Thickness 0.0315 in
|
|
| V-0
@Thickness 1.60 mm
|
V-0
@Thickness 0.0630 in
|
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.80e+17 ohm-cm | 1.80e+17 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.90e+17 ohm | >= 1.90e+17 ohm | ASTM D257 |
| Dielectric Constant | 3.66
@Frequency 1.00e+6 Hz
|
3.66
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| 3.68
@Frequency 60.0 Hz
|
3.68
@Frequency 60.0 Hz
|
ASTM D150 | |
| 3.69
@Frequency 1000 Hz
|
3.69
@Frequency 1000 Hz
|
ASTM D150 | |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | ASTM D149 |
| Dissipation Factor | 0.0010
@Frequency 1000 Hz
|
0.0010
@Frequency 1000 Hz
|
ASTM D150 |
| 0.0020
@Frequency 60.0 Hz
|
0.0020
@Frequency 60.0 Hz
|
ASTM D150 | |
| 0.0030
@Frequency 1.00e+6 Hz
|
0.0030
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 370 – 395 °C | 698 – 743 °F | |
| Mold Temperature | 175 – 210 °C | 347 – 410 °F | |
| Drying Temperature | 150 – 175 °C
@Time 9000 – 14400 sec
|
302 – 347 °F
@Time 2.50 – 4.00 hour
|
|
| Back Pressure | 0.138 – 0.345 MPa | 20.0 – 50.0 psi | |
| Screw Speed | 75 rpm | 75 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Natural | |
| Form | Pellets | |
| Processing Technique | Injection Molding; Machining; Profile Extrusion | |
| RoHS Compliance | RoHS Compliant | |
| Screw Compression Ratio | 2.0:1.0 |