Cossa Polimeri ESTAPROP 1040 V2 H Flame Retardant Polypropylene
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTAPROP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
PP homopolymerFlame retardant class V2, halogen free, good mechanical characteristicsInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.990 g/cc | 0.0358 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.012 – 0.014 cm/cm | 0.012 – 0.014 in/in | ASTM D 955 |
| Melt Flow | 10 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
10 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 28.0 MPa | 4060 psi | ASTM D 638 |
| Elongation at Break | 50 % | 50 % | ASTM D 638 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.200 J/cm
@Temperature 0.000 °C
|
0.375 ft-lb/in
@Temperature 32.0 °F
|
ASTM D 638 |
| 0.300 J/cm
@Temperature 23.0 °C
|
0.562 ft-lb/in
@Temperature 73.4 °F
|
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | 120°C/hr; ASTM D 648 |
| Vicat Softening Point | 155 °C
@Load 0.999 kg
|
311 °F
@Load 2.20 lb
|
50°C/hr; ASTM D 1525 |
| Flammability, UL94 | V-2
@Thickness 1.60 mm
|
V-2
@Thickness 0.0630 in
|
|
| V-2
@Thickness 3.20 mm
|
V-2
@Thickness 0.126 in
|
||
| Glow Wire Test | 960 °C
@Thickness 2.00 mm
|
1760 °F
@Thickness 0.0787 in
|
I.E.C. 695-2-1 |