ELASTO UK Dryflex® 400501S SBS Based Material, 50A Hardness, Natural
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber |
| Manufacturer | ELASTO UK Ltd, a Hexpol company |
| Trade Name | Dryflex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
The 400S-series is a good alternative for indoor applications and disposable articles that do not have high requirements for ageing and heat resistance. The raw materials are specially selected for a fast and stable manufacturing process.Information from Vita Thermoplastic Polymers (VTP).Vita Thermoplastic Polymers was aquired by HEXPOL and is now ELASTO
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0080 – 0.020 cm/cm | 0.0080 – 0.020 in/in | |
| Melt Flow | 8.0 g/10 min
@Load 2.16 kg,
Temperature 190 °C |
8.0 g/10 min
@Load 4.76 lb,
Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 50
@Thickness 4.00 mm
|
50
@Thickness 0.157 in
|
ASTM D2240 |
| Tensile Strength at Break | 2.00 MPa | 290 psi | ASTM D638 |
| Elongation at Break | >= 500 % | >= 500 % | ASTM D638 |
| 100% Modulus | 0.00100 GPa | 0.145 ksi | ASTM D638 |
| 300% Modulus | 0.00200 GPa | 0.290 ksi | ASTM D638 |
| Tear Strength | 20.0 kN/m | 114 pli | ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 75.0 °C | 167 °F | |
| Minimum Service Temperature, Air | -50.0 °C | -58.0 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 170 – 210 °C | 338 – 410 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Bonding to PP | Excellent | |
| Chemical Resistance | Good | Excluding organic solvents, aromatic and vegetable oils |
| Color | Natural | |
| Weather Resistance | Moderate | Air ageing |