Kolon DIAMAT® IG
| Manufacturer | Kolon |
| Trade Name | DIAMAT® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Description: DIAMAT® is a specially formulated high impact grade PMMA resin from KOLON. The acrylic composition results in an excellent balance of impact resistance and high modulus at reasonable pricing. DIAMAT® utilizes acrylic toughener technology resulting in consistent appearance, even after years of UV exposure. DIAMAT® IG is an acrylic molding resin for injection molding, with well balance impact strength and heat resistance. Information provided by US distributor, API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 – 0.0080 cm/cm | 0.0030 – 0.0080 in/in | ASTM D955 |
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 53 | 53 | ASTM D785 |
| Tensile Strength, Ultimate | 44.1 MPa | 6400 psi | ASTM D638 |
| Flexural Strength | 73.8 MPa | 10700 psi | ASTM D790 |
| Flexural Modulus | 2.16 GPa | 313 ksi | ASTM D790 |
| Izod Impact, Notched | 0.422 J/cm | 0.790 ft-lb/in | ASTM D256 |
| Falling Dart Impact | 12.5 J | 9.20 ft-lb |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | Load not specified; ASTM D648 |
| Vicat Softening Point | 95.0 °C | 203 °F | ASTM D1525 |
| Glass Transition Temp, Tg | 105 °C | 221 °F | ASTM D3418 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.49 | 1.49 | ASTM D542 |
| Haze | <= 2.0 % | <= 2.0 % | ASTM D1003 |
| Transmission, Visible | 91 % | 91 % | ASTM D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 150 – 180 °C | 302 – 356 °F | Injection |
| Middle Barrel Temperature | 180 – 230 °C | 356 – 446 °F | Injection |
| Front Barrel Temperature | 210 – 240 °C | 410 – 464 °F | Injection |
| Nozzle Temperature | 220 – 245 °C | 428 – 473 °F | Injection |
| Zone 1 | 200 – 220 °C | 392 – 428 °F | Extrusion |
| Zone 2 | 210 – 230 °C | 410 – 446 °F | Extrusion |
| Zone 3 | 220 – 240 °C | 428 – 464 °F | Extrusion |
| Zone 4 | 210 – 235 °C | 410 – 455 °F | Vent; Extrusion |
| Zone 5 | 225 – 240 °C | 437 – 464 °F | Extrusion |
| Adapter Temperature | 230 – 240 °C | 446 – 464 °F | Extrusion |
| Die Temperature | 220 – 240 °C | 428 – 464 °F | Extrusion |
| Melt Temperature | 220 – 235 °C | 428 – 455 °F | Recommended for Injection |
| Mold Temperature | 40.0 – 80.0 °C | 104 – 176 °F | |
| Roll Temperature | 80.0 – 100 °C | 176 – 212 °F | Extrusion |
| Drying Temperature | 70.0 – 80.0 °C | 158 – 176 °F | |
| Dry Time | 3 – 5 hour | 3 – 5 hour | |
| Injection Pressure | 78.45 – 137.3 MPa | 11380 – 19910 psi | |
| Screw Speed | 40 – 80 rpm | 40 – 80 rpm | Extrusion |