Raschig Group EPOXIDUR® 3580 EP Epoxy
| Manufacturer | Raschig Group |
| Trade Name | EPOXIDUR® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Glass-fiber reinforced and mineral filled epoxy molding compound. Good mechanical strength, very good electrical isolation properties even with thin wall thicknesses and high temperatures. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS).Processing: Injection and compression molding Primary application: Electrical partsInformation provided by the Raschig Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.90 – 2.00 g/cc | 1.90 – 2.00 g/cc | ISO 1183 |
| Apparent Bulk Density | 0.600 – 0.900 g/cc | 0.0217 – 0.0325 lb/in³ | ISO 60 |
| Water Absorption | <= 0.10 %
@Temperature 23.0 °C,
Time 86400 sec |
<= 0.10 %
@Temperature 73.4 °F,
Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0020 – 0.0040 cm/cm | 0.0020 – 0.0040 in/in | (longitudinal) Injection and Compression; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 30.0 – 50.0 MPa | 4350 – 7250 psi | Injection and Compression; ISO 527 |
| Modulus of Elasticity | 14.0 – 16.0 GPa | 2030 – 2320 ksi | Injection and Compression; ISO 527 |
| Flexural Strength | 70.0 – 100 MPa | 10200 – 14500 psi | Injection and Compression; ISO 178 |
| Flexural Modulus | 17.0 – 20.0 GPa | 2470 – 2900 ksi | Injection and Compression; ISO 178 |
| Compressive Strength | 150 – 180 MPa | 21800 – 26100 psi | ISO 604 |
| Charpy Impact Unnotched | 0.400 – 0.600 J/cm²
@Temperature 23.0 °C
|
1.90 – 2.86 ft-lb/in²
@Temperature 73.4 °F
|
Injection and Compression; ISO 179/ 1eU |
| Charpy Impact, Notched | 0.200 – 0.400 J/cm²
@Temperature 23.0 °C
|
0.952 – 1.90 ft-lb/in²
@Temperature 73.4 °F
|
Injection and Compression; ISO 179/ 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 15.0 – 20.0 µm/m-°C
@Temperature 50.0 – 150 °C
|
8.33 – 11.1 µin/in-°F
@Temperature 122 – 302 °F
|
ISO 11359-2 |
| Thermal Conductivity | 0.400 – 0.600 W/m-K | 2.78 – 4.16 BTU-in/hr-ft²-°F | ASTM E1461 |
| Maximum Service Temperature, Air | 180 °C
@Time 7.20e+7 sec
|
356 °F
@Time 20000 hour
|
IEC 60216/T1 |
| 240 °C
@Time <=180000 sec
|
464 °F
@Time <=50.0 hour
|
IEC 60216/T1 | |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 200 °C | >= 392 °F | Injection; ISO 75-B |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 200 °C | >= 392 °F | Injection and Compression; ISO 75-A |
| Deflection Temperature at 8.0 MPa | 180 – 200 °C | 356 – 392 °F | Injection and Compression; ISO 75-C |
| Flammability, UL94 | HB
@Thickness 1.60 mm
|
HB
@Thickness 0.0630 in
|
|
| V-0
@Thickness 6.00 mm
|
V-0
@Thickness 0.236 in
|
||
| Shrinkage | <= 0.050 %
@Temperature 110 °C,
Time 605000 sec |
<= 0.050 %
@Temperature 230 °F,
Time 168 hour |
ISO 2577 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 – 1.00e+16 ohm-cm | 1.00e+15 – 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 – 1.00e+15 ohm | 1.00e+14 – 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 4.0 – 6.0
@Frequency 1.00e+6 Hz
|
4.0 – 6.0
@Frequency 1.00e+6 Hz
|
IEC 60250 |
| 5.0 – 7.0
@Frequency 100 Hz
|
5.0 – 7.0
@Frequency 100 Hz
|
IEC 60250 | |
| Dielectric Strength | 30.0 – 40.0 kV/mm | 762 – 1020 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.010 – 0.030
@Frequency 1.00e+6 Hz
|
0.010 – 0.030
@Frequency 1.00e+6 Hz
|
IEC 60250 |
| 0.030 – 0.050
@Frequency 100 Hz
|
0.030 – 0.050
@Frequency 100 Hz
|
IEC 60250 | |
| Comparative Tracking Index | >= 250 V | >= 250 V | CTI; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Shelf Life | 6.00 Month
@Temperature <=20.0 °C
|
6.00 Month
@Temperature <=68.0 °F
|
| Descriptive Properties | Value | Comments |
|---|---|---|
| Arc Resistance | 4 Stufe | ASTM D495 |
| Glow wire flammability test | 900/1 | IEC 60695 2-12 |
| Glow wire ignitability test | 900/1 | IEC 60695 2-13 |
| Water Absorption | <10 mg | 24h/23°C; ISO 62 |